1 edition of Sodium sulfate corrosion of silicon carbide fiber-reinforced calcium aluminosilicate glass-ceramic matrix composites found in the catalog.
Sodium sulfate corrosion of silicon carbide fiber-reinforced calcium aluminosilicate glass-ceramic matrix composites
Peter J. Newton
1994 by Naval Postgraduate School, Available from National Technical Information Service in Monterey, Calif, Springfield, Va .
Written in English
Hot corrosion effects of Sodium Sulfate (NaSO4) coated Calcium Aluminosilicate (CAS)/Silicon Carbide (SiC) reinforced glass-ceramic matrix composite were investigated using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Analysis (EDX) and X-ray Diffraction (XRD). The samples provided by the Naval Air Warfare Center (NAWC) were unidirectional SiC/CAS as follows: (1) as received, (2) uncoated in air, (3) Na2SO4, coated in air and (4) Na2SO4 coated in argon. A heat treatment was conducted at 900 deg C for 100 hours. Experimental observations indicated that the Na2S04 coating in an oxidising environment had severely corroded the silicon fiber resulting in a silica rich, Nepheline (NaAlSi04), Wollastonite (CaSiO3), Rankinite (CaSi2O7), Albite (NaAlSi3O8 and glassy phases. In the argon atmosphere fiber degradation was present although less severe than in the oxygen environment. Similar phases of silica rich, Nepheline, Albite, Rankinite, Mullite (Al6Si2O13), Pseudo-Wollastonite (CaSiO3) and a glassy region were present. Minimal fiber and matrix degradation was observed in the uncoated sample beat treated in air.
|Statement||Peter J. Newton|
|The Physical Object|
|Pagination||70 p. ;|
|Number of Pages||70|
Appropriate plasters, renders and finishes for cob and random stone walls in Devon
Public school finance in Iowa.
Reflections on that other America
Contracts and payments thereon, Navy Department. Letter from the Acting Secretary of the Navy, replying to House resolution 363, asking information concerning contract and payments thereon under Increase of the Navy and advising as soon as the information can be collated it will be forwarded to the house.
population of Tropical Africa
Secretary of States Consultation for the A2 Particleboard, Oriented Strand Board and Dry Process Fibreboard Sector
Flora of Nigeria
Illustrated bibliographical catalogue of the synapsida
Scale Drawings, 1981-82
Help at hand